Typical Value
 
Grade Purity B2O3 Tot. Oxygen Avg. Particle Size
(D50)
Crystal Size Tap Density  Surface Area (BET)
HC 99% 0.4% 0.5% 9 µm 6 µm 0.3 g/cm3 18 m2/g
HC-W 99.3% 0.1% 0.4% 9 µm 6 µm 0.3 g/cm3 18 m2/g
 Values represent typical data and will vary within ranges established for a particular grade

Applications
 
  ★ To produce special composite ceramic such as Evaporation Boat
  ★ As the raw material for hot pressed BN
  ★ As additive of lubricant coating
  ★ As additive of metal surface treatment
  ★ To produce Cubic Boron Nitride
  ★ As the release agent in shape casting or injection molding process
  ★ As additive in high temperature lubricant oil
 
Characteristics
 
Grade HC is a medium crystal sized with good high temperature resistance and oxidation resistance performance. The crystal size is smaller and some agglomerate to particles with larger size. Due to its round partial agglomerate particle shape, it is very suitable for the application of filler or release agent in shape casting and injection molding process. It is also used to produce composite ceramic and hot pressed BN parts.
Grade HC-W has lower B2O3 content, so it is the perfect choice for the applications that request lower B2O3 contents.