Typical Value
 
Purity B2O3 Total Oxygen Avg. Particle Size (D50) Crystal Size Tap Density Surface Area (BET)
99.4% 0.05% 0.4% 10 µm 10 µm 0.3 g/cm3 10 m2/g
 Values represent typical data and will vary within ranges established for a particular grade

Applications
 
  ★ As filler in thermal conductivity products
  ★ As raw material for BN coating in plasma spray
  ★ As principal raw material in BN coating
  ★ As principal raw material at high temperature insulation composite
  ★ As release agent in optical glass production process
  ★ As additive in premium lubricant oil
  ★ As raw material in hot pressed BN products
 
Characteristics
 
Grade HN is produced up to 1800°C. It has single platelet microstructure and high crystallinity. Those platelets have an average size of app. 9µm and a high aspect ratio. The product is matching the quality of competitive materials manufactured in other parts of the world and can be used as a 1:1 replacement in a lot of established applications. Furthermore, Grade HN has uniform particle size and the particle size is similar to PTFE. Hence it is the perfect additive to be used in high voltage switch nozzle process. Due to its high thermal conductivity, it is a very good fit for thermal conductivity polymer and rubber application. Also very good for high-end BN hot pressed parts with lower oxygen content which is usually less than 0.5%.